fiberglass biaxial fabric have excellent designable Character and great combination character with mat.
Biaxial and multiaxial fabric consists of two or more layers roving fiberglass at different orientations (0, 90, +45, -45), which are stitched together by fine polymer yarn. Standard configurations include biaxial (0,90), (+45,-45), traxial(0,+45,-45) or (90, +45, -45) and multiaxial (0,90,+45,-45).
Because of its excellent designable ability and great combination character with mat perfectly, it is omnipotent with any complex FRP/Composites products needing reinforcement. For instance, wind turbine blade,shipbuilding industry, auto industry, sports apparatus, medical apparatus, the furniture, etc.
SPECIFICATION:
| STYLE | MASS
g/m² | MASS
OZ/YD² | LENGTH
(m) | WIDTHcm | WEIGHT
kg/ROLL | RESIN COMPATIBILITY |
EB450 (0/90) | 450 | 13.3 | 110 | 100 | 49.5 | UP or Epoxy resin |
EB600(0/90) | 600 | 17.7 | 80 | 100 | 48.0 | UP or Epoxy resin |
EB700(0/90) | 700 | 20.6 | 70 | 100 | 49.0 | UP or Epoxy resin |
EB800(0/90) | 800 | 23.6 | 60 | 100 | 48.0 | UP or Epoxy resin |
EB950(0/90) | 950 | 26.5 | 50 | 100 | 47.5 | UP or Epoxy resin |
EB1000(0/90) | 1000 | 29.5 | 50 | 100 | 50.0 | UP or Epoxy resin |
EB1200(0/90) | 1200 | 35.4 | 40 | 100 | 48 | UP or Epoxy resin |
EU400(45/-45) | 400 | 11.8 | 100 | 127 | 50.8 | UP or Epoxy resin |
EU600(45/-45) | 600 | 17.7 | 65 | 127 | 49.5 | UP or Epoxy resin |
ETW750(45/-45/90) | 750 | 22.1 | 50 | 127 | 47.6 | UP or Epoxy resin |
ETL800(0/45/-45) | 800 | 23.6 | 50 | 127 | 50.8 | UP or Epoxy resin |
EMU900(0/45/90/-45) | 900 | 26.5 | 50 | 127 | 57.2 | UP or Epoxy resin |
NOTE
Normally the width is 127cm,it can be cut to any width according to the customers requirements. We can also combinate the chopped strand mat.
PACKING:
Each roll covered by polyethylene plastic bag,then placed into cardboard box. Cardboard box size: 1000mm×260mm×260mm,also can be set on pallet, Each pallet vertical stack 16 cardboard boxes which sizing: 1120mm×1120mm×1150mm.
STORAGE:
Product shall be placed under dryness condition and shall not be opened the covering membrane until applying.